第二部分動態黏彈性分析出最適合的阻尼器材料為添加了10% ASD-MK

第二部分動態黏彈性分析出最適合的阻尼器材料為添加了10% ASD-MK V與90%聚醯脂(polyamides)均勻混合後的阻尼器，動態黏彈性分析結果得出其最大儲存模數為2587.968MPa，最大損失模數為442.789MPa，而最大損耗正切為0.241，最大損耗正切較Pure- polyamides高出59.6%。

結果 (英文) 1:

Part II analysis of dynamic visco-elastic damper materials work best for added 10% ASD-MK v and 90% polyimide resin (polyamides) after mixing damper, dynamic viscoelastic analysis result reached its maximum storage modules for 2587.968MPa, loss modulus of 442.789MPa, and the largest loss tangent is 0.241, maximum loss tangent of 59.6% higher than Pure-polyamides.

結果 (英文) 2:

The second part of the dynamic viscoelastic analysis of the most suitable material for the damper added 10% ASD-MK V and 90% Juxi fat (polyamides) uniformly mixed dampers, dynamic viscoelastic analysis results obtained its maximum storage modulus number 2587.968MPa, the maximum loss modulus 442.789MPa, while the maximum loss tangent of 0.241, the maximum loss tangent was up 59.6% compared with Pure- polyamides.

結果 (英文) 3:

Part two dynamic viscoelastic analysis of the most suitable damper material is added 10% ASD-MK V and 90% poly acyl polyamides after uniform mixing damper, dynamic viscoelasticity analysis results the maximum storage modulus for 2587.968MPa, maximum loss modulus 442.789MPa, and the maximum loss tangent is 0.241, maximum loss tangent is Pure- polyamides higher 59.6% of.